410 Stainless Steel Plate
TISCO, JISCO, BG, ZPSS, YUSCO
7219339000
Size: | |
---|---|
Material: | |
Availability: | |
Quantity: | |
Item: 410 Stainless Steel Sheet
Steel grade: 410
Stainless steel standard: ASTM, AISI, JIS, DIN, EN, GB.
Thickness: 0.1mm-3.0mm (cold rolled), 3.0mm-30mm (hot rolled)
Stainless Steel Sheet width: 1000mm, 1219mm, 1500mm, 1524mm or as per customer's requirement.
Stainless Steel Sheet length: 2000mm, 2440mm, 3000mm, 3048mm or as per customer's requirement.
Stainless Steel Sheet surface: 2B, BA, No. 1, No.4, Hair Line, 8K Mirror or as per customer's requirement.
Stainless Steel Sheet Packing: wooden pallet, iron shelf or as per customer's requirement.
Delivery time: 5-10 working days after received deposit by T/T or L/C term, or according to the different order quantity.
Business term: FOB, C&F, CIF or as per customer's requirement.
MOQ: 1 ton
Application:
Construction field, shipping building industry
Petroleum and chemical industry
Food and machenical industry
Boiler heat exchange
Machinery and hardware industry
Documents: Bill of Lading, packing list, commercial invoice, mill test certificate and any other necessary documents will be provided to customer.
Note: The third party inspection will be acceptable and supported.
Item: 410 Stainless Steel Sheet
Steel grade: 410
Stainless steel standard: ASTM, AISI, JIS, DIN, EN, GB.
Thickness: 0.1mm-3.0mm (cold rolled), 3.0mm-30mm (hot rolled)
Stainless Steel Sheet width: 1000mm, 1219mm, 1500mm, 1524mm or as per customer's requirement.
Stainless Steel Sheet length: 2000mm, 2440mm, 3000mm, 3048mm or as per customer's requirement.
Stainless Steel Sheet surface: 2B, BA, No. 1, No.4, Hair Line, 8K Mirror or as per customer's requirement.
Stainless Steel Sheet Packing: wooden pallet, iron shelf or as per customer's requirement.
Delivery time: 5-10 working days after received deposit by T/T or L/C term, or according to the different order quantity.
Business term: FOB, C&F, CIF or as per customer's requirement.
MOQ: 1 ton
Application:
Construction field, shipping building industry
Petroleum and chemical industry
Food and machenical industry
Boiler heat exchange
Machinery and hardware industry
Documents: Bill of Lading, packing list, commercial invoice, mill test certificate and any other necessary documents will be provided to customer.
Note: The third party inspection will be acceptable and supported.
Chemical Component of Grade 410
Grade | C | Mn | Si | P | S | Cr | Ni |
410 | 0.15 max | 1.00 max | 1.00 max | 0.04 max | 0.03 max | min: 11.5 | 0.50 max |
Physical Properties of Grade 410
Grade | Tensile Strength | Yield Strength | Elongation | Hardness | Hardness |
410 | 65 (450) | 30 (205) | 20 | 217 | 96 |
Heat Treatment | T410 (0.14%C) Hardened 1800°F (982°C) | ||
Rockwell Hardness | 0.2% YS, Ksi (MPa) | UTS, Ksi (MPa) | |
Annealed* | 81 HRB | 45.4 (313) | 80.4 (554) |
Hardened & Tempered 400°F (204°C) | 43 HRC | 156.1 (1076) | 202.9 (1399) |
Hardened & Tempered 550°F (288°C) | 40 HRC | 148.3 (1022) | 187.0 (1289) |
Hardened & Tempered 600°F (316°C) | 40 HRC | 148.8 (1026) | 186.1 (1283) |
Hardened & Tempered 800°F (427°C) | 41 HRC | 132.9 (916) | 188.5 (1300) |
Hardened & Tempered 900°F (482°C) | 41 HRC | 122.6 (845) | 154.3 (1063) |
Hardened & Tempered 1000°F (538°C) | 35 HRC | 127.9 (882) | 154.3 (1063) |
Hardened & Tempered 1200°F (649°C) | 98 HRB | 85.5 (589) | 111.2 (767) |
Chemical Component of Grade 410
Grade | C | Mn | Si | P | S | Cr | Ni |
410 | 0.15 max | 1.00 max | 1.00 max | 0.04 max | 0.03 max | min: 11.5 | 0.50 max |
Physical Properties of Grade 410
Grade | Tensile Strength | Yield Strength | Elongation | Hardness | Hardness |
410 | 65 (450) | 30 (205) | 20 | 217 | 96 |
Heat Treatment | T410 (0.14%C) Hardened 1800°F (982°C) | ||
Rockwell Hardness | 0.2% YS, Ksi (MPa) | UTS, Ksi (MPa) | |
Annealed* | 81 HRB | 45.4 (313) | 80.4 (554) |
Hardened & Tempered 400°F (204°C) | 43 HRC | 156.1 (1076) | 202.9 (1399) |
Hardened & Tempered 550°F (288°C) | 40 HRC | 148.3 (1022) | 187.0 (1289) |
Hardened & Tempered 600°F (316°C) | 40 HRC | 148.8 (1026) | 186.1 (1283) |
Hardened & Tempered 800°F (427°C) | 41 HRC | 132.9 (916) | 188.5 (1300) |
Hardened & Tempered 900°F (482°C) | 41 HRC | 122.6 (845) | 154.3 (1063) |
Hardened & Tempered 1000°F (538°C) | 35 HRC | 127.9 (882) | 154.3 (1063) |
Hardened & Tempered 1200°F (649°C) | 98 HRB | 85.5 (589) | 111.2 (767) |